Single use 5-gram Burstable Twinpaks of Stycast 2850FT/Catalyst 9 with dispense tip.
STYCAST 2850 FT is a two component, thermally conductive epoxy encapsulant that can be used with a variety of catalysts. It features a low coefficient of thermal expansion and excellent electrical insulative properties. The STYCAST 2850 FT Blue is recommended for use in high voltage applications where surface arcing or tracking is a concern. Designed for encapsulation of components which need heat dissipation and thermal shock properties. Catalyst 9 for general purpose with good chemical resistance and physical strength with a viscosity Pa.s cP of 0.080 to 0.105 and 80 to 105.
Burstable TwinPaks feature a frangible (burstable) seal that separates the two components until you are ready to use. Applying deliberate pressure will cause the seal to break or burst, allowing the components to mix together with dispensing tip.
Key Features and Benefits
- Thermal Conductivity
- Low coefficient of thermal expansion
- Dissipation of heat from embedded components
- Low stress on embedded components
Additional information
| Weight | 0.03125 lbs |
|---|---|
| Dimensions | 9 × 7 × 5 in |
| Chemical Composition (%) | Cu: 94.8, Other: Sn 5.0, P 0.2 |
| Density (LB/CU IN) | 0.320 |
| Electrical Conductivity (%IACS @68°F) | 15 |
| Resistivity (OHMS-CIRC. ML/FT) | 69.1 |
| Approximate Melting Point (°F) | 1750 |
| Tensile Strength (KPSI) | Hard:110, Soft: 51 |
| Yield Strength (KPSI) | Hard: 85, Soft: 21 |
| Elongation (%) | Hard: 5, Soft: 49 |
| Hardness | Test Method: ASTM-D-2240, (Value) Unit: Shore D, Catalyst 9: 96 |
| Flexural Strength | Test Method: ASTM-D-790. (Value) Unit: mPa, psi Catalyst 9: 92, 13,300 |
| Compressive Strength | Test Method: ASTM-D-695, (Value) Unit: mPa |
| Linear Shrinkage | Test Method: ASTM-D-2566, (Value) Unit: cm/cm, Catalyst 9: 0.002 |
| Water Absorption (24 hours) | Test Method: ASTM-D-570, (Value) Unit: %, Catalyst 9: 0.03 |
| Coefficient of Thermal Expansion, 1, 2 | Test Method: ASTM-D-3386, (Value) Unit: 10-6/C |
| Glass Transition Temperature | Test Method: ASTM-D-3418, (Value) Unit: °C, Catalyst 9: 86 |
| Thermal Conductivity | Test Method: ASTM-D-2214, (Value) Unit: W/m.K |
| Temperature Range of Use | Test Method: , (Value) Unit: °C, Catalyst 9: -40 to +130 |
| Outgassing(1) TML CVCM | Test Method: ASTM-E-595, (Value) Unit: % |
| Dielectric Strength | Test Method: ASTM-D-149, (Value) Unit: kV/mm |
| Dielectric Constant @ 1 mHz | Test Method: ASTM-D-150, (Value) Unit: –, Catalyst 9: 5.01 |
| Dissipation Factor @ 1 mHz | Test Method: ASTM-D-150, (Value) Unit: –, Catalyst 9: 0.028 |
| Volume Resistivity @ 25°C | Test Method: ASTM-D-257, (Value) Unit: Ohm-cm, Catalyst 9: >1015 |
| Cure Schedule: | 25C: 16-24 hr, 45C: 4-6 hr, 65C: 1-2 hr |
| Shelf Life | 548 Days from the Date of Manufacturing |